Testing materials types

Sample 1 - imitation of such defects as deep disbonds

	Material	plexiglass
	General thickness (mm)	25
	Defect occurrence depth (mm)	8
	Defects square (mm2)	200; 300; 400
	Recommended transducers	RS-1S

Sample 2 - imitation of such defects as disbond between the skin and honeycomb core

	Material	aluminium alloy
	General thickness (mm)	11
	Skin thickness (mm)	0.5
	Honeycomb square (mm2)	40
	Min defect square (mm2)	80
	Recommended transducers	PADI-8S

Sample 3 - imitation of such defects as disbonds

	Material	plexiglass
	General thickness (mm)	8
	Defect occurrence depth (mm)	1.6
	Defect square (mm2)	49; 144; 400
	Recommended transducers	PADI-8S

Sample 4 - imitation of such defects as delaminations

	Material	carbon reinforced plastic
	General thickness (mm)	10
	Defect occurrence depth (mm)	5
	Recommended transducers	RS-1S

Sample 5 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	aluminium alloy
	General thickness (mm)	10
	Skin thickness (mm)	0.8
	Honeycomb square (mm2)	48
	Min defect square (mm2)	100
	Recommended transducers	PADI-8S

Sample 6 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	stainless steel
	General thickness (mm)	26
	Skin thickness (mm)	0.6
	Honeycomb square (mm2)	56
	Min defect square (mm2)	100
	Recommended transducers	PADI-8S

Sample 7 -  imitation of such defects as disbonds between the skin and honeycomb core

	Material	fiber-glass plastic
	General thickness (mm)	20
	Skin thickness (mm)	0.7
	Honeycomb square (mm2)	40
	Min defect square (mm2)	100
	Recommended transducers	PADI-8S

Sample 8 - imitation of such defects as disbonds between the skin and honeycomb core

	Skin material	aluminium alloy
	Honeycomb core material	getinaks
	General thickness (mm)	10
	Skin thickness (mm)	0.8
	Honeycomb square (mm2)	48
	Min defect square (mm2)	100
	Recommended transducers	PADI-8S

Sample 9 - imitation of such defects as disbonds between two bonded metal sheets

	Material	aluminium alloy
	General thickness (mm)	6
	Sheet thickness (mm)	2.95
	Defect square (mm2)	600; 800; 1000
	Recommended transducers	RS-1S

Sample 10 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	fiber glass plastic
	General thickness (mm)	12
	Skin thickness (mm)	1.2
	Honeycomb square (mm2)	35
	Min defect square (mm2)	120
	Recommended transducers	PADI-8S

Sample 11 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	fiber glass plastic
	General thickness (mm)	31
	Skin thickness (mm)	0.5
	Honeycomb square (mm2)	-
	Min defect square (mm2)	-
	Recommended transducers	PADI-8S

Sample 12 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	aluminium alloy
	General thickness (mm)	24
	Skin thickness (mm)	2
	Honeycomb square (mm2)	49
	Min defect square (mm2)	120
	Recommended transducers	PADI-8S

Sample 13 - fragment of helicopter rotor blade, imitation disbond between the layers

	Material	aluminium alloy, rubber, steel
	Recommended transducers	PADI-8S, RS-1S

Sample 14 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	aluminium alloy
	General thickness (mm)	44
	Skin thickness (mm)	2
	Honeycomb square (mm2)	65
	Min defect square (mm2)	150
	Recommended transducers	PADI-8S

Sample 15 - imitation of such defects as disbonds between the three bonded thin metal sheets

	Material	aluminium alloy
	General thickness (mm)	2.5
	Sheet thickness (mm)	0.83
	Min defect square (mm2)	150
	Recommended transducers	PADI-8S

Sample 16 - imitation of such defects as disbonds between the skin and honeycomb core

	Material	carbon reinforced plastic
	General thickness (mm)	11
	Skin thickness (mm)	1
	Honeycomb square (mm2)	28
	Min defect square (mm2)	150
	Recommended transducers	PADI-8S, RS-1S